高强度，抗溶解性，耐磨损，良好的表面光洁度

Radici Compounds PBT100L

聚丁烯对苯二甲酸酯

Radici Plastics USA, Inc.

Technical Data

 

产品说明

 

This is an unreinforced high molecular weight polybutylene terephthalate (thermoplastic polyester) recommended for applications where best toughness and ductility is required. The higher viscosity of this polymer may limit its use in multi-cavity, thin-wall or long-flow path tools. Material exhibits good strength, rigidity and toughness, excellent dimensional stability, resistance to the effects of a very wide range of chemicals, solvents and oils, natural lubricity, wear resistance and easy processability with outstanding part surface appearance.

 

Although grade is shipped in moisture proof packaging, drying prior to processing is strongly recommended to enable best mechanical properties is recommended by MDE.

 

总体

 

材料状态 • 已商用：当前有效

搜索 UL 黄卡 •  Radici Plastics USA, Inc.

供货地区 • 北美洲

添加剂 • 润滑剂

• 尺寸稳定性良好 • 可加工性，良好 • 耐油性能

性能特点 • 高强度 • 良好的表面光洁度 • 韧性良好

• 经润滑 • 耐化学性良好 • 延展性

• 抗溶解性 • 耐磨损性良好 • 粘度，高

外观 • 可用颜色 • 自然色

形式 • 颗粒料

加工方法 • 注射成型

 

物理性能 额定值单位制 测试方法

比重 1.31g/cm³ ASTM D792

收缩率 - 流动 2.0 到 2.2% ASTM D955

吸水率 (饱和) 0.090% ASTM D570

机械性能 额定值单位制 测试方法

抗张强度 (屈服) 55.2MPa ASTM D638

伸长率 (断裂) 250% ASTM D638

弯曲模量 2410MPa ASTM D790

弯曲强度 (屈服) 82.7MPa ASTM D790

冲击性能 额定值单位制 测试方法

悬壁梁缺口冲击强度 (23°C, 3.18 mm) 53J/m ASTM D256

热性能 额定值单位制 测试方法

热变形温度 (1.8 MPa, 未退火) 54.4°C ASTM D648

熔融温度 228°C

注射 额定值单位制

干燥温度 127 到 138°C

干燥时间 2.0 到 3.0hr

建议的最大水分含量 0.050%

螺筒后部温度 260°C

螺筒中部温度 254°C

螺筒前部温度 249°C

加工（熔体）温度 254 到 260°C

模具温度 71.1 到 82.2°C

背压 0.345MPa

螺杆转速 40 到 80rpm

 

 

 

 

 

Radici Plastics聚丁烯对苯二甲酸酯,Radici Plastics PBT,PBT Radici Compounds PBT100L塑料是东莞市双帮塑胶原料有限公司常年销售的塑料，因为塑料价格行情每天都有新变化前天的报价不等于今天的报价。本公司销售的所有原料保证是原厂原包,随料可以提供生产厂商提供的物性表、SGS报告，ROHS报告，REACH报告  SVHC报告，COA出厂报告,提供原料注塑加工工程中可能出现的各种异常现象解决方法，塑料牌号太多，本网站没有提供的本公司也有代理，详情请咨询本公司相关业务人员0769-87795123  微信：13549213581     联系电话：13549213581肖生